Jis Z 1707 -

Established by the Japanese Standards Association (JSA), JIS Z 1707 has undergone multiple revisions to adapt to advancements in polymer technology. The most recent major revisions occurred in the late 1990s and early 2000s, aligning with global trends toward thinner, stronger films with better environmental stability.

Protective sheeting for machinery, floor protection during renovation, and temporary weather barriers.

Compare with:

Gap analysis: [e.g., JIS Z 1707 draft lacks high-temperature performance criteria found in ISO.]

The standard also groups films by nominal thickness: jis z 1707

Note: Thickness tolerances are strictly enforced, typically within ±10% of nominal value.

| Property | Type 1 (General) | Type 2 (Heavy-duty) | |----------|----------------|---------------------| | Tensile strength (MD) | ≥ 19.6 MPa | ≥ 24.5 MPa | | Tensile strength (TD) | ≥ 17.7 MPa | ≥ 22.6 MPa | | Elongation at break (MD) | ≥ 200% | ≥ 250% | | Elongation at break (TD) | ≥ 300% | ≥ 350% | Established by the Japanese Standards Association (JSA), JIS

(MD = Machine Direction, TD = Transverse Direction)